he impact of thermal treatment on the properties of bentonites from the Kalzhat and Orta Tentek deposits was examined. The samples were analyzed using XRD, XRF, TGA/DSC, and lowtemperature nitrogen adsorption (BET) before and after heating at temperatures ranging from 100 to 900°C. Moderate heating at 200–300°C removes physically adsorbed water and part of the interlayer water without affecting the layered structure of montmorillonite, which retains its specific surface area, water-holding capacity, and cation-exchange capacity. In the 400–600°C range, dehydroxylation and interlayer collapse occur, resulting in a decrease in specific surface area and the loss of exchange sites. At 700–900°C, high-temperature silica and aluminosilicate phases form, and the porosity approaches zero. The comparison of the two deposits reveals that the Orta Tentek bentonites undergo structural degradation earlier than the Kalzhat bentonites, with the latter exhibiting greater resistance to degradation during the initial stages of heating.; However, at elevated temperatures, both materials cease to perform their agronomic functions. To utilize them as soil conditioners, it is recommended to restrict the treatment to a temperature range of 200–300°C, with brief exposure times, followed by granulation. It is crucial to avoid temperatures exceeding 400–600°C and to completely exclude temperatures above 700–900°C. These conditions ensure a sanitary pretreatment without compromising the soil's moisture retention or cation exchange capacity. This approach is particularly suitable for sandy and sandy-loam soils in the arid regions of Kazakhstan.DOI
https://doi.org/10.52081/bkaku.2025.v75.i4.287Практическое значение
Практическая значимость исследования заключается в определении оптимальных режимов термической обработки бентонитовых глин месторождений Калжат и Орта-Тентек для их эффективного применения в качестве почвоулучшителей. Установлено, что обработка при температурах 200–300°C обеспечивает санитарную подготовку материала без существенной потери влагоудерживающей способности и катионообменной емкости. Полученные результаты могут быть использованы в сельском хозяйстве для повышения плодородия песчаных и супесчаных почв засушливых регионов Казахстана, а также при разработке технологий подготовки и гранулирования бентонитовых материалов.Данный документ располагается в коллекциях
Публикации в КОКСОН
Файлы документа
journal_author_tS5eqYs8mXfy5db.pdf